SE1310A/B is high strength 2-part liquid silicone rubber

1) Basic model:SE1310A/B

2) Product Description

    SE1310A/B is high strength 2-part liquid silicone rubber,catalyzed by platinum, it is made up of basic compound / crosslinking agent / catalyst / fillings and additives,it doesn’t contain heavy metal and aromatic hydrocarbons dissolvent, it is nonhazardous to human body.

3) Key Features

  Environment-friendly, Innoxious, Pollution-free, Good rebound,

  Good adherence to fabric. 

4) Application

Be used for making logo sheet.

5) Storage:The products should be closed tightly, protected from light and moisture.

6) How to use:The curing agent is SE1310B, the using ratio is SE1310A:SE1310B=10:1. The typical curing condition is 130°Cx10-15mins, the curing time should be coordinated by the thickness of the products.

7) Packaging

    The product is available in 20kgs pailsl

8) Typical properties

Property	Unit	Value
Viscosity	mPa.s	A:5.6X104,A+B:4.0x104 A:B(middle speed)=10:1
Shore A hardness	°A	34
Tensile strength	MPa	4.0
Tear Strength	KN/M	9.8
Elongation at break	%	300
Linear shrinkage rate	%	2.60
Tensile set	%	1.08
Rebound		69

9)Remarks

Prohibit contacting such organics as N/P/S  and  plasma chemical compound  like  Sn/Pb/Hg/Bi/ As,also the chemical compound including acetylene series and vinylidene, to avoid uncureing caused by platinum catalyst poisoning. Especially, prohibit contacting PVC,since it contains Pb,which will also lead to catalyst poisoning.The mixing SE1310A and SE1310B should be used up within 12 hours, or it will cause cross bonding andcuring gradually, then lead to uneffectiveness of the mixing, if the temperature increased, it should be made special attention.

The organic pigment will also lead to slower in curing time even uncuring.

The figures are for reference only, Please contact us for detail.