CM1017 |
|||||
|
|
|||||
|
性能項目 |
測試條件 |
測試方法 |
數值/描述 |
單位 |
|
|
機械性能 |
拉伸強度(引張強度) |
|
ASTM D638/ISO 527 |
|
kg/cm²(MPa)[Lb/in2] |
|
斷裂伸長率 |
|
ASTM D638/ISO 527 |
|
% |
|
|
拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm²(MPa)[Lb/in2] |
|
|
拉伸屈服伸長率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
|
拉伸斷裂伸長率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
|
彎曲模量(彎曲彈性率) |
|
ASTM D790/ISO 178 |
|
kg/cm²(MPa)[Lb/in2] |
|
|
彎曲強度 |
|
ASTM D790/ISO 178 |
|
kg/cm²(MPa)[Lb/in2] |
|
|
洛氏硬度 |
|
ASTM D785 |
83 |
|
|
|
IZOD 缺口衝擊強度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
|
1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
Charpy衝擊強度 |
23℃ （缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
|
-30℃（缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
23℃（無缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
-30℃（無缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
|
物性性能 |
比重（密度） |
|
ASTM D792/ISO 1183 |
1.13 |
|
|
成型收縮率 |
|
ASTM D955 |
|
% |
|
|
熔融指數（流動係數） |
200℃/5kg |
ASTM D1238/ISO 1133 |
|
g/10min |
|
|
220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
||
|
吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
1.8 |
% |
|
|
熱性能 |
熱變形溫度 |
退火 |
ASTM D648/ISO 75 |
190 |
℃（℉） |
|
未退火 |
ASTM D648/ISO 75 |
|
℃（℉） |
||
|
維卡軟化點 |
|
ASTM D1525/ISO R306 |
|
℃（℉） |
|
|
熔點 |
|
- |
225 |
℃（℉） |
|
|
燃燒性（率） |
|
UL94 |
|
|
|
|
線性膨脹係數 |
|
ASTM D696/ISO 11359 |
|
mm/mm.℃ |
|
|
電氣性能 |
介電常數 |
100HZ |
ASTM D150/IEC 60250 |
|
|
|
1MHZ |
ASTM D150/IEC 60250 |
|
|
||
|
體積電阻率 |
|
ASTM D257/IEC 60093 |
10^12~13 |
Ω.cm |
|
|
表面電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω |
|
|
耐電弧性 |
|
ASTM D495/IEC 60112 |
|
|
|
|
加工條件 |
乾燥條件 |
|
|
|
|
|
加工溫度 |
射嘴 |
|
|
℃ |
|
|
料筒前段 |
|
|
℃ |
||
|
料筒中段 |
|
|
℃ |
||
|
料筒後段 |
|
|
℃ |
||
|
熔體溫度 |
|
|
|
℃ |
|
|
模具溫度 |
|
|
|
℃ |
|
|
壓力 |
注塑壓力 |
|
|
Mpa |
|
|
保壓壓力 |
|
|
Mpa |
||
|
背壓 |
|
|
Mpa |
||
|
螺杆轉速 |
|
|
|
rpm |
|
|
其他 |
備註 |
|
|||
|
顏色 |
|
||||
|
特性 |
|
||||
|
用途 |
|
||||
| 付款方式︰ | TT |
|---|---|