產品描述
| 簡介 |
高溫合金GH132/A-286/SUH660/S66286/1.4980,現已納入國家GB1221-92耐熱鋼系列.應用範圍,650℃下使用的高溫部件，具有高的屈服強度和持久、蠕變強度，並有良好的加工塑性和滿意的焊接性能. |
| |
| |
| |
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
牌號 |
|
|
|
|
|
|
|
|
|
|
|
| |
GH2132(GH132) |
|
|
|
|
|
|
|
|
|
|
| |
中國 |
0Cr15Ni25Ti2MoAIVB |
|
|
|
|
|
|
|
|
|
| |
國外牌號 |
A-286 |
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
化學成分 |
|
|
|
|
|
|
|
|
|
|
|
| |
C |
Si |
Mn |
P |
|
|
|
|
|
|
|
|
| |
≤0.08 |
≤1.00 |
1.00～2.00 |
≤0.030 |
|
|
|
|
|
|
|
|
| |
S |
Ni |
Cr |
Mo |
|
|
|
|
|
|
|
|
| |
≤0.020 |
24.0～27.0 |
13.5～16.0 |
1.00～1.50 |
|
|
|
|
|
|
|
|
| |
Al |
Ti |
Fe |
其他 |
|
|
|
|
|
|
|
|
| |
≤0.40 |
1.80～2.35 |
余量 |
V：0.10～0.50;B：0.001-0.010； Co：≤1.0 |
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
機械性能 |
|
|
|
|
|
|
|
|
|
|
|
| |
δ0.2 [N/平方毫米] |
δb [N/平方毫米] |
δ5 [%] |
ψ [%] |
|
|
|
|
|
|
|
|
| |
≥60kgf/平方毫米 |
≥92/mm |
≥15 |
≥20 |
|
|
|
|
|
|
|
|
| |
硬度 |
|
|
|
|
|
|
|
|
|
|
|
| |
- |
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
合金牌號 |
交貨狀態的熱處理制度 |
室溫硬度HB(d)mm（Hv） |
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
| |
GH2132(GH132) |
980-1000℃,水（油）冷 |
≥4.25（194） |
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
合金牌號 |
熱處理制度 |
瞬時拉伸性能 |
硬度HB(d)mm（Hv） |
持久性能 |
| |
溫度℃ |
σb kgf/mm2 |
σ0.2 kgf/mm2 |
δ5% |
ψ% |
溫度℃ |
應力 kgf/mm2 |
斷裂時間h |
δ5% |
| |
GH2132(GH132) |
交貨狀態+700-720℃16小時，空冷 |
室溫 |
≥92 |
≥60 |
≥15 |
≥20 |
3.30-3.85（260-360） |
650 |
46 |
≥23 |
≥5 |
| |
（≥95） |
|
（≥18） |
（≥40） |
3.30-3.85（260-360） |
650 |
{40} |
{100} |
|